配方类型: | CERAMICS AND GLASS |
配方说明: | Typical Compositions of Glass Fluxes 9% Oxide Compositions) |
配方组成: | Al2O3/- Formula No.1 Na2O/4.4 TiO2/4.0 Li2O/- Li2O/- ZrO2/- Na2SiF6/- Firing Temperature (F)/1120 Firing Temperature (C)/604 Coefficient of Expansion (X10^-^7)/89 Lead Solubility (parts per million)/40 Alkali Resistance/Good PbO/45.5 B2O3/2.2 CdO/- SiO2/36.3 Al2O3/- CdO/4.3 Na2O/4.8 TiO2/4.9 Li2O/2.0 ZrO2/- Na2SiF6/- Firing Temperature (F)/1100 Firing Temperature (C)/593 Coeffici |
配制方法: | Note: cs indicates complete solubility. |