配方类型: | CEMENT AND RELATED PRODUCTS |
配方说明: | Caulking Compounds |
配方组成: | Talc/3.50 or 100.00 % by Wt The caulk was mixed in a sigma blade mixer. "Indopol" Polybutene, butyl rubber solution and drying oil were added and mixed well (5-10 minutes). Then the fillers were slowly added to the mixing vehicle in the order shown above. After the addition of titanium-calcium pigment, the mass was mixed to a smooth paste (about 35 minutes). the drier was added along with sufficient mineral spirits to obtain the desired consistency. Mixing was continued un |
配制方法: | The caulk was mixed in a sigma blade mixer. INDOPOL Polybutene and drying oil were added and mixed well (5-10 minutes). Then the fillers were slowly added to the mixing vehicle in the order shown above. After the addition of titanium-calcium pigment, the mass was mixed to a smooth paste (about 35 minutes). the drier was added along with sufficient mineral spirits to obtain the desired consistency. Mixing was continued until the mass was uniform (about 3-5 minutes). |